Obtención y caracterización de un material dental mediante el proceso de infiltración de un vidrio de composición leucítica sobre una matriz de alúmina

Usma Gutiérrez, Jorge Iván (2013) Obtención y caracterización de un material dental mediante el proceso de infiltración de un vidrio de composición leucítica sobre una matriz de alúmina. Maestría thesis, Universidad Nacional de Colombia, Sede Medellín.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB

Resumen

Resumen: En esta investigación se obtuvo un material compuesto de alúmina infiltrada con un vidrio de composición leucítica. Tres tipos de probetas de alúmina se infiltraron con el mismo vidrio, con fines de evaluar el efecto de la distribución de tamaños de partícula sobre las propiedades mecánicas del material. La composición molar del vidrio empleado en la infiltración fue 14.09% K2O - 2.11% Al2O3 - 46.22% SiO2 - 24.31% CaO - 7.73% Na2O - 0.18% B2O3 - 0.2% TiO2 - 5.14% CeO2. La fuente de Al2O3 empleada en el vidrio provino de un caolín colombiano al igual que parte del SiO2 y el CaO se adicionó como wollastonita. El vidrio se obtuvo a través del método de fusión a 1200°C. Tanto la sinterización de las matrices, como la infiltración del vidrio sobre la matriz de alúmina se realizaron a 1200°C empleando una velocidad de calentamiento de 5°C/min desde la temperatura ambiente. El material compuesto obtenido presentó propiedades mecánicas mejoradas con respecto a la alúmina sinterizada, evidenciándose que el vidrio empleado en la infiltración actuó como un agente de refuerzo del material. Se sugiere que las propiedades mecánicas del material están favorecidas en mayor proporción, por variables como la distribución de tamaño de grano, siendo los menores tamaños de grano los que inducen mejores propiedades mecánicas al material, Abstract: In this research, an alumina composite infiltrated with a leucite composition glass was obtained. Three types of alumina samples were infiltrated with the same glass in order to evaluate the effect of the particle size distribution on the mechanical properties of the material. The molar composition of the glass used in infiltration was 14.09% K2O - 2.11% Al2O3 - SiO2 46.22% - 24.31% CaO - 7.73% Na2O - B2O3 0.18% - 0.2% TiO2 - 5.14% CeO2. Colombian kaolin became the source of Al2O3 and part of SiO2 in glass. All CaO was added as wollastonite. The glass was obtained by melting at 1200°C. Both the sinterization and glass infiltration were performed at 1200°C using a heating rate of 5 °C/min from room temperature. The obtained composite material had improved mechanical properties respect to the sintered alumina, so it can be showed that the glass acted as a reinforcing agent material. It can be established that the mechanical properties of the material depends on the grain size distribution, now that lower grain sizes induce better mechanical properties to the material

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:García, Claudia Patricia
Información adicional:Magíster en Ciencias - Química
Palabras clave:Material compuesto, vidrio infiltrado, leucita
Temática:5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
Unidad administrativa:Sede Medellín > Facultad de Ciencias
Código ID:9585
Enviado por : Jorge Iván Usma Gutiérrez
Enviado el día :05 Julio 2013 17:45
Ultima modificación:05 Julio 2013 17:45
Ultima modificación:05 Julio 2013 17:45
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox