Efecto del arenado en la resistencia a la flexión y a la fractura de dos zirconios con dos áreas de sección transversa

Calvo Ramírez, Juan Norberto and Díaz Hurtado, Janeth and Oviedo Hernández, Nataly Alexandra (2015) Efecto del arenado en la resistencia a la flexión y a la fractura de dos zirconios con dos áreas de sección transversa. Acta Odontológica Colombiana, 5 (1). pp. 13-23. ISSN 2027-7822

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

782kB

URL oficial: https://revistas.unal.edu.co/index.php/actaodontoc...

Resumen

Introducción: el zirconio estabilizado con Itrio es un material cerámico considerado como alternativa “estética” en prótesis parcial fija. Estudios clínicos han evidenciado microfracturas en la zona de los conectores, desprendimiento de la cerámica de recubrimiento y dificultades en el acondicionamiento para cementarse. Objetivo: establecer la influencia del arenado en la resistencia flexural y a la fractura de dos cerámicas de zirconio-itrio con dos áreas de sección transversa. Materiales y métodos: se diseñaron y sinterizaron 40 barras de 25mm de longitud de dos materiales (IPS e.max ZirCAD y VITA Inceram YZ), 20 de 2x2mm±0.02 y 20 de 3x3mm±0.03 en la sección transversa; diez muestras de cada grupo se arenaron con óxido de aluminio de 50μ a 2.5bares. Cada espécimen fue cargado hasta su fractura, en una máquina de ensayos universal, a una velocidad de 1±0.5mm/min. Los datos fueron analizados mediante la prueba t student. Resultados: la cerámica e.max ZirCAD mostró la mayor resistencia flexural (1232.78MPa) y la mayor carga a la fractura (802,74N). Al arenarse VITA Inceram YZ tuvo una mayor resistencia a la flexión (906.85MPa) y soportó una mayor carga 565,55N. La prueba t student indicó diferencias estadísticamente significativas en el grupo e.max ZirCAD al arenarse, tanto en resistencia flexural como a la fractura, en las dos áreas. No hubo diferencias estadísticamente significativas entre las dos cerámicas, tanto en las dos áreas de sección transversa como al tratamiento de superficie. Conclusiones: el arenado disminuye significativamente los valores de resistencia a la flexión y a la fractura de las dos cerámicas en las dos áreas de sección transversa., Background: Yttrium stabilized zirconia a ceramic material currently considered as an “aesthetic” alternative in fixed partial denture. Clinical studies they have shown micro fractures in the area of the connectors, detachment or “chipping” ceramic coating and also the difficulties in fitting for her cementing. Objective: To establish the influence of sandblasting on flexural strength and fracture toughness of two Yttrium stabilized zirconia with two cross- sectional areas. Material and methods: Two materials were tested VITA Inceram YZ and IPS e.max ZirCAD, for each material was obtained 20 bars of 25mm in length, 2x2mm±0.02 width and height and 20 bars of 3x3mm±0.03 width and height. The samples were sintered; ten samples of each group were subjected to surface treatment with sandblasting. Each specimen was loaded to fracture in a Universal Testing Machine with a transverse head speed of 1±0.5mm/min. The data were analysed with the t student test. Results: The zirconia e.max ZirCAD has the highest flexural strength (1232.78 MPa) and the load-bearing fracture (802.74N). Surface treatment VITA Inceram YZ had a higher flexural strength (906.85 MPa) and supported a major load 565,55N. The test t student indicated statistically significant differences in the group IPS e.max ZirCAD when it is sandblasting, so much in the resistance to the flexion, since in the maximum load up to the fracture in both areas. There were no statistically significant differences between two ceramics, it having considered both cross-section areas and surface treatment (with and without sandblasting). Conclusions: Sandblasting, the values flexural strength and fracture toughness of the two ceramics in the two areas of cross section significantly decreasing.

Tipo de documento:Artículo - Article
Palabras clave:Yttria stabilized zirconia, sandblasting, flexural strength, fracture load, linear shrinkage., zirconio-itrio, arenado, resistencia a la flexión, sección transversa, contracción lineal
Temática:6 Tecnología (ciencias aplicadas) / Technology > 61 Ciencias médicas; Medicina / Medicine & health
Unidad administrativa:Revistas electrónicas UN > Acta Odontológica Colombiana
Código ID:60173
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :28 Noviembre 2017 14:52
Ultima modificación:28 Noviembre 2017 14:52
Ultima modificación:28 Noviembre 2017 14:52
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox