Wear resistance of vanadium-niobium carbide layers grown via TRD

Castillejo-Nieto, Fabio Enrique and Olaya-Florez, Jhon Jairo and Alfonso, José Edgar (2015) Wear resistance of vanadium-niobium carbide layers grown via TRD. DYNA, 82 (193). pp. 104-109. ISSN 2346-2183

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB

URL oficial: https://revistas.unal.edu.co/index.php/dyna/articl...

Resumen

Nb-V complex carbide coatings were produced on AISI D2 steel substrates using the thermo-reactive diffusion (TRD) process in order to improve the surface hardness and wear resistance of this tool steel. The carbide coating treatment was performed using molten borax with added ferroniobium, ferrovanadium, and aluminum at temperatures of 1223, 1293, and 1363 K for 2, 3, 4, and 5 h. The coating layers were characterized with scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS). The growth rates of the coatings were studied, and a kinetic model of the layer thickness was constructed as a function of the time and temperature treatment. The hardness and friction coefficient (COF) of the coatings was measured through nanoindentation and pin on disk test respectively. The carbide layers had a homogeneous thickness and a hardness of 37.63 GPa, which is close to values obtained in superhard materials, and the COF was in the range of 0,3 for the coated steels.

Tipo de documento:Artículo - Article
Palabras clave:Thermo Reactive Diffusion, Niobium-Vanadium Carbide, Hardness, wear
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Revistas electrónicas UN > Dyna
Código ID:58983
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :31 Oct 2017 17:20
Ultima modificación:27 Noviembre 2017 22:05
Ultima modificación:27 Noviembre 2017 22:05
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox