Comportamiento de un recubrimiento bicapa de Cr/CrN bajo degradación por erosión-corrosión por ensayo de impacto con chorro

Alegría Ortega, Johanna Andrea and Ocampo-Carmona, Luz Marina and Rodríguez, Fernando and Forlerer, Elena (2016) Comportamiento de un recubrimiento bicapa de Cr/CrN bajo degradación por erosión-corrosión por ensayo de impacto con chorro. DYNA, 83 (197). pp. 145-152. ISSN 2346-2183

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB

URL oficial: https://revistas.unal.edu.co/index.php/dyna/articl...

Resumen

La técnica de deposición catódica fue utilizada para depositar un recubrimiento bicapa de Cr/CrN sobre acero AISI 440C. La morfología y composición del recubrimiento fueron evaluadas con microscopía electrónica de barrido y difracción de rayos-x. La dureza y adhesión del recubrimiento también fueron estudiadas. Se siguió el procedimiento de la norma ASTM G-119 para evaluar el desgaste por erosión-corrosión usando un chorro de lodo impactando a 90° a una velocidad de 4 y 8 m/s para impactar sobre el acero desnudo y recubierto. Los resultados muestran que el sinergismo es la componente de desgaste más agresiva, ésta excede en un 40% la pérdida de masa total para el acero recubierto y el 60% de la pérdida de masa total para el acero desnudo. El incremento en la velocidad de impacto incrementa la pérdida de masa tanto en el acero desnudo como en el recubierto. Comparando, el recubrimiento de Cr/CrN presentó mayor resistencia a la corrosión y al desgaste por erosión–corrosión., Cathodic arc technique was used to deposit a Cr/CrN bilayer coating on AISI 440C stainless steel. The morphology and composition of the coating were verified by Scanning Electron Microscope and X-Ray Diffraction. Hardness and adhesion of the coating were also studied. In the erosion-corrosion wear, a slurry jet with impingement angle 90° at 4 and 8 m/s was used to impact upon bare and coated steel. All the wear mechanisms were evaluated according to ASTM G-119. The results indicate that the synergism wear rate is the most aggressive wear component, exceeding 40% of the total mass loss for coating steel and 60% of mass loss for bare steel. An increase in the impact velocity increases mass loss for both bare and coated steel. In comparison, the Cr/CrN coating had better corrosion and erosion–corrosion resistance.

Tipo de documento:Artículo - Article
Palabras clave:Multilayer coating, Staintess Steel, Cathodic Arc, erosion-corrosion, Recubrimientos multicapas, Acero inoxidable, Arco catódico, erosión-corrosión
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Revistas electrónicas UN > Dyna
Código ID:58865
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :31 Oct 2017 17:20
Ultima modificación:27 Noviembre 2017 22:04
Ultima modificación:27 Noviembre 2017 22:04
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox