Obtención del compuesto Mg2Ni0.5Co0.5 mediante aleado mecánico y estudio de su comportamiento frente al proceso de hidruración

Martínez Ugalde, Carola Andrea and Ordoñez, Stella and Guzmán, Danny and Serafini, Daniel and Rojas, Paula and Aguilar, Claudio (2017) Obtención del compuesto Mg2Ni0.5Co0.5 mediante aleado mecánico y estudio de su comportamiento frente al proceso de hidruración. DYNA, 84 (200). pp. 240-246. ISSN 2346-2183

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

772kB

URL oficial: https://revistas.unal.edu.co/index.php/dyna/articl...

Resumen

Este trabajo presenta la evolución microestructural del compuesto Mg2Ni0,5Co0,5 obtenido mediante aleado mecánico y el estudio de sus propiedades de hidruración. Los polvos elementales de Mg, Ni y Co con una relación atómica 2:0,5:0,5 se alearon mecánicamente en un molino de alta energía Spex 8000D por 36 h (muestra amorfa) y posteriormente se realizó un tratamiento térmico a 673 K por 15 min (muestra nanocristalina). La caracterización de las muestras amorfas y nanocristalinas se realizó mediante difracción de rayos-X. El proceso de hidruración fue realizado por técnica volumétrica Sievert a 363 K y una presión de H2 de 2 MPa. El proceso de desorción se evaluó por calorimetría diferencial de barrido. Basados en los resultados obtenidos podemos concluir que la estructura amorfa absorbe más hidrógeno, alcanzando un máximo de 3,6%  en peso de H2. Los eventos presentes en el proceso de desorción depende de si la aleación es amorfa o nanocristalina., This work presents the microstructural evolution of mechanically alloyed Mg2Ni0.5Co0.5 and a study of its hydriding properties. Mg, Ni, and Co elemental powders (atomic ratios of 2:0.5:0.5, respectively) were mechanically alloyed in a Spex 8000D high-energy mill for 36 h (amorphous sample) and subsequently submitted to a thermal treatment at 673 K for 15 min (nanocrystalline sample). The characterizations of the samples were performed with X-ray diffraction. A Sievert-type volumetric hydriding process was done at 363 K and with hydrogen pressure of 2 MPa. Desorption process was evaluated through differential scanning calorimetry. Based on the obtained results, it is possible to conclude that the amorphous structure absorbs more hydrogen, reaching a maximum of 3.6 wt. % H. Desorption process events depend on amorphous or nanocrystalline states.

Tipo de documento:Artículo - Article
Palabras clave:Hydrogen Storage, Nanostructured Materials, Mechanical Alloying, Magnesium, Almacenadores de Hidrógeno, Materiales Nanoestructurados, Aleado Mecánico, Magnesio
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Revistas electrónicas UN > Dyna
Código ID:58747
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :31 Oct 2017 17:19
Ultima modificación:27 Noviembre 2017 22:03
Ultima modificación:27 Noviembre 2017 22:03
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox