Remoción de hidrocarburos de aguas de producción de la industria petrolera utilizando nanointermedios compuestos por SiO2 funcionalizados con nanopartículas magnéticas

Villegas, Juan P and Arcila, Neyda and Ortega, Diana and Franco, Camilo A. and Cortés, Farid (2017) Remoción de hidrocarburos de aguas de producción de la industria petrolera utilizando nanointermedios compuestos por SiO2 funcionalizados con nanopartículas magnéticas. DYNA, 84 (202). pp. 65-74. ISSN 2346-2183

Texto completo

[img]
Vista previa
PDF - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

URL oficial: https://revistas.unal.edu.co/index.php/dyna/articl...

Resumen

El principal objetivo de este trabajo es desarrollar nanointermedios compuestos por un soporte micrométrico de SiO2 funcionalizado con nanopartículas magnéticas para la adsorción de hidrocarburos emulsionados en agua. SiO2 con tamaño < 20 μm fue funcionalizada con nanopartículas de magnetita de 97 nm en una relación de 5% p/p. La eficiencia del nanointermedio fue evaluada mediante experimentos de adsorción por lotes bajo diferentes condiciones de temperatura, pH, salinidad y concentración de crudo. Tanto para el soporte de SiO2 como para el nanointermedio, la cantidad máxima de adsorción se alcanza para tiempos inferiores a 100 minutos. Las capacidades adsortivas del nanointermedio fueron comparadas utilizando un material comúnmente empleado en la industria petrolera. Adicionalmente, los materiales pueden ser regenerados mediante procesos térmicos para su posterior reutilización. Se observó que la inclusión de las nanopartículas de magnetita al soporte de SiO2 proporciona un efecto catalítico en la descomposición de los hidrocarburos adsorbidos., This work aims to develop nano-intermediates adsorbents based on micrometric silica functionalized with magnetite nanoparticles with high efficiencies in the oil removal, additionally to high catalytic activities in the decomposition of the crude oil adsorbed. Silica with sizes < 20 μm were functionalized with 5 wt% of magnetite nanoparticles. The efficiency of the adsorbents was evaluated through batch adsorption experiments of oil from oil in water emulsions at different pH, salinity and oil concentration using a UV-vis spectrophotometer. Results showed that for both the SiO2 support and the synthesized nano-intermediate, the adsorption equilibrium was reached in less tan 100 min. A comparison was made by employing a material typically used in the oil and gas industry. After the adsorption process, the materials can be recovered and regenerated trough thermal processes. It was observed that the magnetite nanoparticles over the support act as a catalyst for decomposition of the adsorbed oil.

Tipo de documento:Artículo - Article
Palabras clave:Production water, Adsorption, Nano-Intermediates, Oil, Pyrolysis, Oxidation, Agua de Producción, Adsorción, Nanointermedio, Petróleo, Pirólisis, Oxidación
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Revistas electrónicas UN > Dyna
Código ID:58700
Enviado por : Dirección Nacional de Bibliotecas STECNICO
Enviado el día :31 Oct 2017 17:19
Ultima modificación:27 Noviembre 2017 22:02
Ultima modificación:27 Noviembre 2017 22:02
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox