Efecto de la microestructura sobre la resistencia al desgaste por rodadura-deslizamiento de aceros ferroviarios

Zapata Orozco, Diego Alberto (2011) Efecto de la microestructura sobre la resistencia al desgaste por rodadura-deslizamiento de aceros ferroviarios. Maestría thesis, Universidad Nacional de Colombia, Sede Medellín.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial Share Alike.

3MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

3MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB
[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

3MB

Resumen

Se llevaron a cabo tratamientos térmicos sobre el acero de ruedas R8 con el fin de obtener una microestructura perlitica homogénea con dureza y características similaresa las de fabricación, sobre el clásico acero R-260 y el moderno acero 370LHT empleados en la fabricación de rieles, en busca de obtener microestructuras perliticas y bainiticas con niveles de dureza similares (350HV- 370HV). Se realizo caracterización metalografía de las microestructuras mediante microscopia óptica y electrónica de barrido, además de una evaluación de las propiedades mecánicas sobre las microestructuras de los aceros de rieles por medio de tomas de dureza, ensayos a tracción, ensayos de impacto Charpy y ensayos de tenacidad a la fractura. Se fabricaron probetas de dichas microestructuras con geometría y dimensiones especificas para ser evaluadas en la maquina disco-disco bajo condiciones de presión y acabado superficial definidas, logrando analizar el desempeño de las mismas a rodadura pura y rodadura deslizamiento. Características de las grietas bajo la superficie de cada microestructura fueron mostradas, además relaciones entre pérdida de masa y propiedades mecanicas fueron establecidas, identificando las propiedades de mayor influencia en la resistencia a fatiga superficial sobre las microestructuras ensayadas bajo condiciones especificas de contacto.Abstract. The R8 wheel steel was conveniently heat treated to obtain pearlitic microstructure characteristics with hardness values similar to those of actual wheels in commercial railroad systems; in the same way, both classic R260 and modern 370LHT rail steels were submitted to proper heat treatments to obtain pearlitic and bainitic microstructures with hardness values in the range, i.e. 350 HV and 370 HV. Microstructural analyses were performed using scanning electron and light optical microscopy; also mechanical properties by means of hardness, tensile, Charpy impact and fracture toughness tests of those rail microstructures were assessed. Test specimens with specific geometry and dimensions were obtained from those microstructures; they were tested in the disc-on-disc wear testing machine under hertzian contact pressure and surface roughness well defined, analyzing their wear performance in pure rolling and rolling-sliding contacts. In this study, cracks characteristics below the rail specimen’s surfaces were showed, correlating loss weight and mechanical properties relationships, with the aim to identify those properties with strongly influence on the rolling contact fatigue resistance under contact conditions previously established.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Toro, Alejandro
Palabras clave:Fatiga superficial; Rodadura; Deslizamiento; Microestructura; Máquina disco-disco/Rolling contact fatigue; Rolling; Sliding; Microstructure; Twin disc machine.
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales
Código ID:5481
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :24 Enero 2012 21:59
Ultima modificación:11 Oct 2012 21:11
Ultima modificación:11 Oct 2012 21:11
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox