Desarrollo de un procedimiento de soldadura para juntas de acero de blindaje mil a 46100 con proceso gmaw / Development of a welding procedure for mil a 46100 armor steel joints using gas metal arc welding

Mazuera Robledo, David and Suárez Gómez, Jhon Alberto and Giraldo Barrada, Jorge Enrique (2011) Desarrollo de un procedimiento de soldadura para juntas de acero de blindaje mil a 46100 con proceso gmaw / Development of a welding procedure for mil a 46100 armor steel joints using gas metal arc welding. Dyna, 78 (168). pp. 65-71. ISSN 0012-7353

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

Se desarrolló un procedimiento de soldadura (WPS) para unir láminas de acero para blindaje bajo especificación MIL A46100 usando el proceso GMAW, el cual fue calificado mediante ensayos mecánicos y no destructivos (NDT) de acuerdo con los requerimientos de códigos militares. Los resultados obtenidos fueron comparados con procedimientos de soldadura para este material realizados con el proceso SMAW. Los resultados obtenidos mostraron que el WPS diseñado es una opción viable para la soldadura de blindajes de acero MIL A 46100. Además, con el WPS diseñado se obtuvo una reducción en el ancho de la zona afectada térmicamente (ZAT) que debería conducir a un mejor desempeño en servicio de los blindajes de acuerdo con los resultados de estudios previos. Finalmente, se encontró un incremento en la energía absorbida en los ensayos de impacto Charpy V comparada con la de soldaduras realizadas con el proceso SMAW./ Abstract. A welding procedure (WPS) for MIL A46100 steel armor joints using the gas metal arc welding process (GMAW) was developed and qualified according to mechanical and non-destructive (NDT) requirements of military codes. Obtained results were compared to shielded metal arc welding (SMAW) procedures used to weld this type of steel. It was found that designed WPS is a suitable option to weld MIL A46100 armors according to the results obtained. In addition, a narrower heat affected zone (HAZ) was obtained with designed WPS which should lead to a better in-service armor performance according to results of previous studies. Finally, an increase in Charpy v-notch (CVN) test impact energy compared to the SMAW procedure was found.

Tipo de documento:Artículo - Article
Palabras clave:Acero para blindaje MIL A 46100; Especificación del procedimiento de soldadura (WPS); Soldadura por arco con protección gaseosa (GMAW) / Gas metal arc welding (GMAW); Welding procedure specification (WPS); MIL A 46100 armor steel
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales
Código ID:5447
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :12 Enero 2012 22:14
Ultima modificación:12 Enero 2012 22:14
Ultima modificación:12 Enero 2012 22:14
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox