Análisis del efecto de algunos parámetros en el proceso de electroformado de piezas cilíndricas de niquel a escala mili./Effect analysis of some parameters in the electroforming process of niquel cylindrical part at mili scale.

Vélez, Santiago and Cardona, Andrés Felipe and Gaviria, Juan and Vélez, Juan and González, Javier (2007) Análisis del efecto de algunos parámetros en el proceso de electroformado de piezas cilíndricas de niquel a escala mili./Effect analysis of some parameters in the electroforming process of niquel cylindrical part at mili scale. Dyna, 74 (153). pp. 203-213. ISSN 0012-7353

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

275kB

Resumen

En este trabajo se caracterizaron piezas cilíndricas de níquel electroformadas a partir de un baño Watts con corriente directa en moldes de acrílico. Se evaluó la influencia de la densidad de corriente, la relación de aspecto y el régimen de flujo sobre las características de las piezas. La caracterización incluyó: conformación externa e interna, análisis de microestructura y análisis de microdureza. Bajo todas las condiciones de operación se lograron piezas con un buen acabado superficial y adecuada reproducción del molde acrílico. El análisis conformacional reveló que los defectos se ubican preferentemente en la parte interna y hacia el último tercio del crecimiento. Las piezas más homogéneas y con menos defectos fueron las depositadas con densidad de corriente de 10 A dm-2 y velocidad de flujo 10 mm s-1 en un molde de 0.4 mm de diámetro. Los valores de dureza se ubicaron alrededor de 250 HV, pero se encontraron valores de hasta 400 HV./Abstract: In this work cylindrical nickel pieces electroformed from an standard Watts bath with direct current in acrylic moulds were characterised. The influence of current density, aspect ratio and flow regime on the piece’s characteristics was evaluated. The characterisation included: external and internal conformation analysis, microstructure and microharness analysis. Pieces with a good superficial finish and adequate acrylic mould reproduction where obtained under all tested conditions. The conformational analysis revealed that the defects were located preferably in the internal part and toward the last third of the growth. The most homogeneous and with less defects pieces were those deposited with current density 10 A dm-2, bath speed 10 mm s-1 and diameter 0.4 mm. Hardness values were located around 250 HV, but values up to 400 HV were observed.

Tipo de documento:Artículo - Article
Palabras clave:Proceso LIGA; Electrodepositación; Densidad de corriente; Relación de aspecto; Régimen de flujo.
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas
Código ID:5379
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :12 Enero 2012 22:34
Ultima modificación:12 Enero 2012 22:34
Ultima modificación:12 Enero 2012 22:34
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox