Incidencia del material cementante (cemento-cal) en el retemplado de un mortero hidráulico

González Willianson, Ricardo (2015) Incidencia del material cementante (cemento-cal) en el retemplado de un mortero hidráulico. Maestría thesis, Universidad Nacional de Colombia - Sede Medellín.

Texto completo

[img]
Vista previa
PDF - Versión Enviada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

5MB

Resumen

Resumen: el retemplado consiste en adicionar agua para recuperar la consistencia de la mezcla antes de iniciar su fraguado. El agua adicionada por retemplado es función del agua perdida por evaporación antes del fraguado inicial, y su relación varía según la dosificación del material cementante. El objetivo de la investigación fue identificar cómo incide la dosificación del material cementante (cal/cemento) sobre el retemplado de un mortero hidráulico. Para conseguirlo, fue necesario, en distintos tiempos de retemplado, encontrar la cantidad de agua que recuperaba la consistencia de la mezcla, así como su relación con el agua evaporada, al cambiar la proporción de cal en el material cementante. En consecuencia, se prepararon morteros con tres proporciones de cal en relación al material cementante: 5%, 10% y 25%. Se evaluaron tres tiempos de retemplado: 1,5 horas, 2,5 horas, y 3,5 horas. A su vez, se consideraron dos condiciones de evaporación en cada tiempo de retemplado: media (CE1) y alta (CE2). Los morteros se fabricaron para una consistencia especificada: fluidez de 110%. Se concluyó que en condiciones similares de evaporación, la proporción del material cementante incide sobre el retemplado de la siguiente manera: al incrementar el contenido de cal de 5% a 10% se necesitó adicionar mayor cantidad de agua para recuperar la fluidez inicial de 110%, pero al seguir aumentando la cal hasta el 25%, la tendencia se invirtió, reflejando el efecto de la retención de agua producida por la cal sobre la evaporación; este comportamiento se observó en todos los tiempos de retemplado. Los resultados encontrados proponen una posible relación entre la velocidad de evaporación y el contenido de cal en el material cementante., Abstract: the retempering consists in adding water to recover the consistency of the mixture before it starts setting. The water added by retempering is a function of the water lost to evaporation before the initial setting, and its ratio varies depending on the dosage of the cementing material. The aim of the research was to identify how this affects the dosage of cementitious material (lime / cement) on retempering a hydraulic mortar. To achieve this, it was necessary, in different periods of retempering, to find the amount of water recovered by the consistency of the mixture, as well as the relationship with the evaporated water, when changing the proportion of lime in the cementitious material. Consequently, mortars were prepared with three proportions of lime relative to cementitious material: 5%, 10% and 25%. Three periods of retempering were evaluated, 1,5 hours, 2,5 hours, and 3,5 hours. In addition two conditions of evaporation were considered in each period of retempering: medium (EC1) and high (CE2). The mortars were made to a specified consistency: fluidity of 110%. It was concluded that under similar conditions of evaporation, the proportion of cementitious material affects the retempering as follows: when increasing the lime content from 5% to 10% more water was needed to recover the initial fluidity of 110%, but in further increasing the lime content to 25%, the trend was reversed; this behavior was observed in all the periods of retempering. The results suggest a possible relationship between the evaporation rate and the lime content in the cementitious material

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Ochoa Botero, Juan Carlos
Información adicional:Maestría en Construcción Línea de Investigación: Tecnología
Palabras clave:Retemplado, Consistencia, Fluidez, Evaporación, Mortero, Cal, Retempering, Consistency, Fluidity, Evaporation, Mortar, Lime
Temática:6 Tecnología (ciencias aplicadas) / Technology > 69 Construcción / Building & construction
Unidad administrativa:Sede Medellín > Facultad de Arquitectura > Escuela de Construcción
Código ID:51972
Enviado por : bdigital1_ med
Enviado el día :20 May 2016 19:47
Ultima modificación:20 May 2016 19:47
Ultima modificación:20 May 2016 19:47
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox