Caracterización de la tenacidad de fractura bajo la norma ASTM E 399-08 (PROBETA SENB), en aceros AISI-SAE 5160 H, utilizado en fabricación de ballestas

Martínez Romero, Juan Carlos (2011) Caracterización de la tenacidad de fractura bajo la norma ASTM E 399-08 (PROBETA SENB), en aceros AISI-SAE 5160 H, utilizado en fabricación de ballestas. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB
[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB
[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB
[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

3MB
[img] PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB

Resumen

La fractura de materiales de ingeniería es casi siempre un hecho indeseable por varias razones, tales como la seguridad de vidas humanas, pérdidas económicas y la interferencia con la disponibilidad de productos y servicios. La industria automotriz ha estado siempre a la vanguardia en investigación ya que el mercado cada vez es más competido y exige productos de confiabilidad y de bajo costo. Los fabricantes y usuarios de ballestas desean buen desempeño, durabilidad y una reducción en el peso ya que esto se refleja en el consumo de combustible, por lo cual es más competitivo fabricar ballestas que ofrezcan la mayor tolerancia al daño posible, y con una alta tenacidad de fractura se asegura una mayor vida útil de las ballestas ante la presencia de discontinuidades. / Abstract. This project evaluates the behavior of fracture toughness in specimens of AISISAE 5160H steel used in the manufacture of automotive leaf spring. Specimens from four suppliers were subjected to quenched and tempered from seven different temperatures. The specimens were precracking in fatigue machine and subject to fracture toughness test in SENB settings, creating fracture surfaces, which were classified and inspected macroscopically (to simple view and in stereoscopic) and microscopic (scanning electron microscope-SEM). The material was characterized by chemical analysis, hardness and metallography. Ruled in Standard E399-08 was selected the type of specimen, was determined the precracking assembly and the fracture toughness was calculated in terms of Jtotal and Jcritical. With the development of this project found that the tempered temperature influenced the fracture toughness and was evident that one of the providers had a strong performance at lower fracture toughness than the other three suppliers.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Espejo Mora, Edgar
Información adicional:Magíster en Ingeniería, Materiales y Procesos
Palabras clave:TE Resistencia a la Fractura; AISI-SAE 5160H; Templado y Revenido; ASTM E399-08; J Integral / Fracture Toughness TE; AISI-SAE 5160H; Quenched and Tempered; ASTM E399-08; J Integral
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecánica
Sede Medellín > Facultad de Minas > Escuela de Mecatrónica > Ingeniería Mecánica
Código ID:5131
Enviado por : Universidad Nacional de Colombia Biblioteca Digital - Sede Bogotá
Enviado el día :09 Noviembre 2011 19:43
Ultima modificación:09 Noviembre 2011 19:43
Ultima modificación:09 Noviembre 2011 19:43
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox