Estudio experimental del comportamiento magnético de multicapas Cr/Gd/Cr no homogéneas

Jaramillo Morales, Juan Fernando (2014) Estudio experimental del comportamiento magnético de multicapas Cr/Gd/Cr no homogéneas. Maestría thesis, Universidad Nacional de Colombia - Sede Manizales.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB

Resumen

En este trabajo, estudiamos el comportamiento magnético a baja temperatura y cerca de la temperatura critica, TC (que se encuentra muy próxima a la temperatura ambiente) de muestras de Cromo - Gadolinio - Cromo (Cr/Gd/Cr) no homogéneas, usando medidas de magnetización DC. Las muestras se prepararon en forma de multicapas Cr(50nm)/Gd(100nm)/Cr(50nm) sobre sustratos monocristalinos de Si(110) por medio de la técnica pulverización catódica asistida. Posteriormente, las muestras fueron sometidas a un tratamiento térmico (recocido) a diferentes temperaturas (TAN), TAN = 200, 400, y 500°C, durante 10 minutos, para controlar su in-homogeneidad, y la magnetización de las muestras se midió por medio de un magnetómetro de muestra vibrante (VSM) usando los procesos enfriamiento a campo cero (ZFC) y enfriamiento con campo (FC), los cuales se realizaron para diferentes valores de campo. Encontrando que el comportamiento magnético de las muestras es compatible con un estado ferromagnético, que experimenta una transición de fase ferro–paramagnética (F-P) alrededor de la temperatura crítica, TC, la cual es muy próxima a la temperatura ambiente. Sin embargo, para temperaturas por debajo de TC, observamos diferencias entre la magnetización medida durante el enfriamiento a campo cero (MZFC) y el enfriamiento con campo (MFC). La MFC disminuye con el incremento de la temperatura, mientras que la MZFC aumenta con el incremento de la temperatura y, además de la transición de fase FP a TC, exhibe un pequeño pico en una determinada temperatura TG<TC. Encontramos también, que la MZFC es dependiente del tiempo a campo bajo e irreversible por debajo de la temperatura de irreversibilidad, Ti(H). Determinamos y analizamos también diferentes parámetros claves del comportamiento magnético de las muestras a través de los ciclos de histéresis, tales como, campo coercitivo, campo de cierre y magnetización de saturación, Abstract : In this work, the low-temperature phase and critical behavior at high temperature of inhomogeneous chromium – gadolinium-chromium samples were investigated using DC magnetization measurements. The samples were prepared as Cr(50nm)/Gd(100nm)/Cr(50nm) multilayers grown onto Si(110) single crystal substrates by means of sputter deposition. The samples in-homogeneity was controlled by annealing at different temperatures TAN=200, 400, and 500°C during 10 minutes and their magnetization of the samples by a vibrating sample magnetometer (VSM)was measured using zero field cooling (ZFC) and field cooling (FC) procedures at several applied fields. Approximately room temperature, the magnetic behavior of the samples is compatible with a ferromagnetic ground state, which undergoes a rounded ferromagnetic (F)-paramagnetic (P) phase transition at a critical temperature, TC. At temperatures below TC, however, differences between the magnetization measured in the zero field cooling (MZFC) and field cooling (MFC) procedures are observed. MFC decreases with increasing temperature. MZFC increases with increasing temperature and, in addition to the F-P phase transition at TC, shows a peak at a certain temperature TG<TC. It was also found that MZFC is time dependent at low field and irreversible below an irreversible temperature Ti(H). We determine and analyze different key parameters of the magnetic behavior of the samples through the cycles of hysteresis, coercive field, field of closure, and saturation magnetization

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Información adicional:Tesis de investigación presentada como requisito parcial para optar al título de : Magíster en Ciencias-Física -- Línea de Investigación : Materia Condensada - Magnetismo
Palabras clave:Magnetización, Gadolinio, Multicapas, Temperatura crítica, Transición de fase, Comportamiento magnético, Magnetómetro de muestra vibrante, Materiales magnéticos, Magnetization, Gadolinium, Multilayers, Critical temperature, Phase transition, Magnetic behavior, Vibrating sample magnetometer, Magnetic materials
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
6 Tecnología (ciencias aplicadas) / Technology
Unidad administrativa:Sede Manizales > Facultad de Ciencias Exactas y Naturales > Departamento de Física y Química
Código ID:47534
Enviado por : Biblioteca Digital Universidad Nacional de Colombia - Sede Manizales
Enviado el día :24 Mar 2015 10:16
Ultima modificación:24 Mar 2015 10:16
Ultima modificación:24 Mar 2015 10:16
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox