Resistencia flexural de la zirconia monolítica sometida a diferentes tratamientos de superficie

Vanegas Nieto, Ana Camila (2014) Resistencia flexural de la zirconia monolítica sometida a diferentes tratamientos de superficie. Otra thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

8MB

Resumen

OBJETIVO Determinar el efecto de cuatro tratamientos de superficie y de las dimensiones del conector, en la resistencia flexural de barras de dos marcas comerciales de zirconia monolítica, por medio de un ensayo mecánico que permita establecer cambios positivos o negativos en el comportamiento biomecánico de la cerámica. MATERIALES Y MÉTODOS Se probaron 50 barras sinterizadas de zirconia monolítica de dos casas fabricantes diferentes, simulando un conector de una PPF con 4 tratamientos de superficie y un grupo control. Se realizó una prueba de resistencia flexural de tres puntos variando la posición de las muestras en una máquina universal de ensayos mecánicos a una velocidad de cabeza transversa de 1 mm/s. Los datos fueron registrados y sometidos a un análisis de varianza ANOVA de 1 y 2 vías p=<0,05 y al test de Tukey para encontrar correlación entre todas las variables. RESULTADOS La dimensión de altura de las muestras afectó significativamente la resistencia a la carga flexural de la zirconia monolítica, no hubo diferencias estadísticamente significativas entre los valores de resistencia a la flexión de los grupos con tratamiento de superficie Vs. el grupo control. La marca comercial no afectó de manera significativa la resistencia a la flexión de las muestras. CONCLUSIONES Independientemente de la marca comercial, la altura del conector afecta significativamente la resistencia a la carga de flexión de la zirconia monolítica, a mayor altura, mayor resistencia a la flexión. Los tratamientos de superficie afectan el comportamiento de la zirconia monolítica frente al grupo control sin encontrarse diferencias significativas entre si., Abstract. OBJECTIVE Determining the effect of four surface treatments and connector dimensions on the flexural strength of two monolithic zirconia trademarks, by applying a mechanical test to establish positive or negative changes in the biomechanical behavior of ceramics. MATERIALS AND METHODS 50 sintered monolithic zirconia bars from two different manufacturers were tested, simulating a FPP connector with 4 surface treatments and a control group. A test of threepoint flexural strength was carried out by varying the position of the samples in a universal mechanical testing machine to a transverse head speed of 1 mm / s. Data were recorded and subjected to analysis of variance of 1 and 2-way p=0,05, and Tukey test to find correlation between all the variables. RESULTS The height dimension of the samples significantly affects the flexural load resistance of the monolithic zirconia, no statistically significant differences between the values of flexural strength of the surface treating groups Vs. the control group were found. Trademark not significantly affects the flexural strength of the samples. CONCLUSIONS Regardless of trademark, the height of the connector significantly affect the resistance to flexural load of the monolithic zirconia, higher heights have greater resistance to bending. Surface treatments affect the behavior of monolithic zirconia vs. the control group, however no significant differences between them were found.

Tipo de documento:Tesis/trabajos de grado - Thesis (Otra)
Colaborador / Asesor:Calvo Ramírez, Juan Norberto and Amaya Rey, Gonzalo
Información adicional:Rehabilitador Oral. Línea de Investigación: Biomateriales dentales
Palabras clave:Zirconia, Óxido de zirconio, Zirconio estabilizado con itrio, Fenómenos mecánicos, Propiedades mecánicas, Resistencia flexural, Zirconia oxide, Zirconium oxide, Ytria stabilized tetragonal zirconia, Mechanical phenomena, Mechanical properties, Flexural strenght
Temática:6 Tecnología (ciencias aplicadas) / Technology > 61 Ciencias médicas; Medicina / Medicine & health
Unidad administrativa:Sede Bogotá > Facultad de Odontología
Código ID:46976
Enviado por : bdigital4_ bog
Enviado el día :12 Febrero 2015 09:04
Ultima modificación:12 Febrero 2015 09:04
Ultima modificación:12 Febrero 2015 09:04
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox