Desarrollo de una resina estructurada tipo núcleo-coraza (pigmento- polímero) con agente acoplador tipo silano para pinturas base agua de alto desempeño

Amaya Molina, Luis Daniel (2014) Desarrollo de una resina estructurada tipo núcleo-coraza (pigmento- polímero) con agente acoplador tipo silano para pinturas base agua de alto desempeño. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

4MB

Resumen

Los polímeros en emulsión se emplean en la fabricación de pinturas plásticas en base agua para unir y adherir el producto a un sustrato o soporte. Las resinas copolímeras dan el carácter de la pintura y de ellas dependen en su mayoría las características finales de esta. Se desarrolla una resina estructurada que constituye de un núcleo de vinil acetato acoplado por medio de un agente silano (Viniltrimetoxisilano) a partículas de dióxido de titanio; con una coraza compuesta por un copolímero de vinil acetato, 2 etil hexil acrilato e hidroxietil metacrilato. En un vinilo tipo 1, el núcleo duro aporta una mayor resistencia al rayado y ranurado, relacionado con el aumento en el contenido de pigmento inorgánico, mientras que el desempeño de características como la resistencia al lavado, al agua, a los álcalis y la adherencia recaen en la coraza blanda que mejora al aumentar el contenido del monómero blando (2 etil hexil acrilato). La formulación, caracterización y evaluación del desempeño de las pinturas obtenidas se hace de acuerdo a las pruebas referenciadas en la norma técnica colombiana NTC 1335 (pinturas al agua tipo emulsión) y para el caso de las resinas estructuradas se emplean algunas de las pruebas presentes en la norma técnica colombiana NTC 1774 (Emulsiones homopolímeras y copolímeras) junto al uso de técnicas de análisis como la distribución de tamaño de partículas, difracción de rayos X, microscopía electrónica de barrido, sortometría, calorimetría diferencial de barrido, análisis termogravimétrico y zetametría, Abstract. The polymers in emulsion are used in the manufacture of latex paints waterborne or architectural vinyl to unite and adhere to the product a substrate or a support. The resins copolymers give the nature of the paint, and the most final features of the painting depend on them. As a response to the needs of this industry develops a resin that is structured by a core of vinyl acetate coupled trough a silane agent (vyniltrimethoxysilane) to particles of titanium dioxide; with a shell composed of a copolymer of vinyl acetate, 2 ethyl hexyl acrylate, and hydroxyethyl methacrylate. In a vinyl type 1, the hard core brings the most resistance to scratching and gouging related with the increase of the content of inorganic pigment, while .The performance features such as resistance to washing, water, alkalis and adherence relapse into the soft shell that is improved by increasing the content of the soft monomer (2 ethyl hexyl acrylate). As a result of this structure, it is obtained a resin that improves some of the properties of a vinyl related to the wear which could decrease the content of polymer resins derived from petroleum in a vinyl or improve the performance decrease this repaint cycles and a more durable product. The formulation, characterization and evaluation of the performance of the paintings obtained ,it is done according to the testing and contained and referenced in the technical Colombian standard NTC 1335 (water paint emulsion type) and for the case of the resins are used structured some of the evidence present in the technical Colombian standard NTC 1774 (Emulsions homopolymers and copolymers).Also, the use of techniques of analysis and the size distribution of particles, X-ray diffraction, scanning electron microscopy, sorptometer analysis, differential scanning calorimetry, thermogravimetric analysis and z potential analysis.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Boyacá Mendivelso, Luís Alejandro
Información adicional:Magister en Ingeniería Química. Línea de Investigación: Procesos de Polimerización y Materiales
Palabras clave:Resina vinil acrílica, Agente acoplador tipo silano, Dióxido de titanio, Vinilo tipo 1, Emulsiones estructuradas, Vinyl acrylic resin, Silane coupling agent, Titanium dioxide, Vinyl type 1, Structured emulsions
Temática:6 Tecnología (ciencias aplicadas) / Technology > 66 Ingeniería química y Tecnologías relacionadas/ Chemical engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Química y Ambiental
Código ID:46802
Enviado por : bdigital4_ bog
Enviado el día :10 Febrero 2015 10:51
Ultima modificación:10 Febrero 2015 10:51
Ultima modificación:10 Febrero 2015 10:51
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox