Optimización de soportes de Colágeno tipo I como un sistema de entrega controlada para un extracto de caléndula (Calendula officinalis).

Jiménez Cruz, Ronald Andrés (2014) Optimización de soportes de Colágeno tipo I como un sistema de entrega controlada para un extracto de caléndula (Calendula officinalis). Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

En Colombia existe la necesidad de desarrollar productos de ingeniería de tejidos de costo moderado que sean efectivos, seguros y estables para el tratamiento de pérdidas tejidos y órganos. El grupo de ingeniería de tejidos del departamento de Farmacia de la Universidad Nacional, ha desarrollado soportes de colágeno y tejidos artificiales que al ser usados como injerto en heridas de espesor parcial mejoran la regeneración de tejidos blandos. Una alternativa sencilla y menos costosa de tratamiento es asociar soportes de colágeno con un extracto de flores caléndula (Calendula officinalis), aceptado por el INVIMA como antioxidante y cicatrizante de uso tópico. En este trabajo se optimizaron los soportes de colágeno tipo I mediante la incorporación de micropartículas de gelatina-colágeno, modificación que aumento la capacidad de asociación con el extracto de C. officinalis de los soportes, mejoro la resistencia a la degradación enzimática y en estudios de liberación in vitro modifico el mecanismo de liberación de metabolitos secundarios que componen el extracto de C. officinalis., Abstract. Aiming to develop acellular collagen type I matrices with an improved biological performance in the treatment of skin wounds, scaffolds were modified with microspheres and the subsequent loading of an extract of marigold Calendula officinalis -flower rich in polyphenols. These compounds have shown anti-inflammatory and antioxidant activities that are beneficial in wound healing processes. Microspheres made of poly(vinyl alcohol), gelatin and mixtures of poly(vinyl alcohol)-collagen and gelatin-collagen were produced by a water-in-oil emulsion/cross-linking method. Their morphology, size distribution, swelling rate and ability to associate with the extract were characterized. Gelatin-collagen microspheres swelled and showed the highest capacity to load the extract and thus, they were chosen to be incorporated into collagen suspensions at three growing concentrations (1.0 mg/mL, 2.5 mg/mL and 5.0 mg/mL) to manufacture collagen scaffolds including gelatin-collagen microspheres. Resistance to enzymatic degradation, ability to associate with the extract, and release profile of the three gelatin-collagen microsphere-scaffold prototypes were assessed, including scaffolds without microspheres as controls. Data indicated that gelatin-collagen microspheres increased the scaffolds' resistance to enzymatic degradation in vitro, as well as their association with the flower extract. Finally, the microspheres prolonged the release of the extract supporting their potential application in therapy of skin wounds.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Información adicional:Magister en Ciencias Farmacéutica
Palabras clave:Colágeno tipo I, Soportes, Calendula officinalis, Micropartículas, Ingeniería de tejidos, Collagen I scaffolds, polymeric microspheres, Calendula officinalis extract, Polyphenols, Controlled release
Temática:5 Ciencias naturales y matemáticas / Science > 54 Química y ciencias afines / Chemistry
6 Tecnología (ciencias aplicadas) / Technology > 61 Ciencias médicas; Medicina / Medicine & health
Unidad administrativa:Sede Bogotá > Facultad de Ciencias > Departamento de Farmacia
Código ID:43391
Enviado por : bdigital4_ bog
Enviado el día :31 Oct 2014 13:34
Ultima modificación:31 Oct 2014 13:34
Ultima modificación:31 Oct 2014 13:34
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox