Estudio del mecanismo de opacificación de un recubrimiento cerámico

Cardona Restrepo, Lorena (2013) Estudio del mecanismo de opacificación de un recubrimiento cerámico. Maestría thesis, Universidad Nacional de Colombia - Sede Medellín.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

6MB

Resumen

Resumen: Un engobe es un recubrimiento cerámico que se aplica comúnmente sobre las baldosas y precede la aplicación del esmalte. Los engobes deben ser opacos y blancos con el fin de uniformar y con frecuencia, cubrir el tono del soporte arcilloso. Comprender el fenómeno de la opacidad en estos recubrimientos implica considerar la interacción de la luz con las partículas que se encuentran inmersas en la matriz. En el presente trabajo se estudió el mecanismo de opacificación en un engobe a la luz de la interacción entre sus componentes. Como composición base se tomó una formulación tradicional, a la que se le varió el tipo de frita y el componente opacificante usado (silicato de circonio), reemplazándolo por mezclas de materiales alternativos. Como sustitutos se utilizaron tres tipos de alúmina de diferente tamaño de partícula y cristalinidad, óxido de cinc y dos tipos de silicato de circonio. Se aplicó un diseño de mezclas combinado con un factor adicional, no composicional (tipo de frita) con el fin de establecer el efecto de los componentes sobre las características deseadas en el engobe. Como variables respuesta se midieron el índice de blancura, las coordenadas colorimétricas, la reflectancia difusa a 460nm, la permeabilidad y brillo medido a 60º. El análisis por medio de difracción de rayos X y microscopía electrónica de barrido de algunas de las muestras, permitió discernir que el mecanismo de opacificación de un engobe cerámico puede depender de la inmiscibilidad de partículas, desvitrificación a partir de la frita, la reactividad con consecuente formación de fases, de los componentes adicionados con la frita y de los componentes entre sí, y ocasionalmente, de la separación de fases vítreas., Abstract: An engob is a ceramic coating which is commonly applied on the tiles. It precedes the glaze application. The engobs should be opaque and white in order to homogenize and often cover the clay paste color. Understanding the phenomenon of opacity in these coatings involves the interaction of light with particles that are embedded in the matrix. In the present work, it was studied the mechanism of opacification in an engob considering the interaction between its components. A standard composition was used as a reference. It was changed the frit type and it was replaced the main opacifying component (zirconium silicate) by mixtures of alternative materials. Three types of alumina with different particle size and crystallinity, zinc oxide and two types of zirconium silicate were incorporated in the mixture. The experimentation was planned by combining mixture and factorial designs in order to study the effect of the frit type and the components on the desired characteristics of the engob. The measured response variables were whiteness index, the colorimetric coordinates, the diffuse reflectance at 460nm, permeability and brightness measured at 60º). The microstructure analysis of some samples by X-ray diffraction and scanning electron microscopy, allowed to discern the opacification mechanism in a ceramic engob. The engob opacity may be due to the immiscibility of particles, devitrification of phases from the frit, reactivity of the components with other components or with the frit to form crystalline phases and occasionally, it may be caused by the vitreous phase separation.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:García García, Claudia Patricia
Información adicional:Maestría en Ingeniería de Materiales y Procesos
Palabras clave:Opacidad, Blancura, Fase cristalina, Engobe, Fase vítrea, Silicato de circonio, Alúmina, Opacity, Whiteness, Crystalline phase, Vitreous phase, Zirconium
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
6 Tecnología (ciencias aplicadas) / Technology > 69 Construcción / Building & construction
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales
Código ID:43098
Enviado por : Unnamed user with email lcardonr@unal.edu.co
Enviado el día :02 Oct 2014 12:15
Ultima modificación:02 Oct 2014 12:15
Ultima modificación:02 Oct 2014 12:15
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox