Influencia de la intensidad del plasma y la velocidad de alimentación de aluminio sobre la difusión del oxigeno y el agua en peliculas de polipropileno biorientado recubiertas con aluminio / Plasma´s intensity and aluminum´s feed rate influence on diffusion rate to oxygen and water vapor in bi-oriented polypropylene films coated with aluminum

Gutiérrez Bernal, Jesús Manuel (2011) Influencia de la intensidad del plasma y la velocidad de alimentación de aluminio sobre la difusión del oxigeno y el agua en peliculas de polipropileno biorientado recubiertas con aluminio / Plasma´s intensity and aluminum´s feed rate influence on diffusion rate to oxygen and water vapor in bi-oriented polypropylene films coated with aluminum. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

3MB

Resumen

Dentro de los materiales utilizados como empaques por la industria alimenticia, están las películas con base polímero y metalizadas, con el fin de crear barreras de difusión al oxigeno y al agua, elementos que son responsables del deterioro de los alimentos. Dentro de estos materiales, el polipropileno ocupa un lugar importante y por lo tanto es necesario buscar experimentalmente elementos que ayuden a la buena formación de esas películas. El tratamiento que se le dé a la película, antes del recubrimiento superficial con aluminio, afecta de manera notoria las propiedades de adhesión entre sustrato y depósito, influenciando la velocidad de difusión al oxígeno y al agua. En este trabajo se caracterizaron las películas de polipropileno biorientado (BOPP) metalizadas con aluminio, con una sola formulación, y con un tratamiento de tipo plasma previo a la metalización, buscando, entre las posibles causas la que más influye en la velocidad de difusión al oxigeno y al agua. Lo anterior se realizó, primero identificando, con calorimetría diferencial de barrido (DSC), las materias primas utilizadas en la producción de las muestras utilizadas, y segundo con ensayos de microscopia electrónica de barrido (SEM), difracción de rayos X, microscopia de fuerza atómica (AFM), y ensayos de barrera, según las normas ASTM D3985 y F1249. / Abstract. Among the materials used like packs in the food industries, there are the films with polymeric bulk and metalized to create diffusion barriers to oxygen and water vapor, which are responsible for food spoilage. Among these materials, the polypropylene is very important and therefore need search experimentally ways that help to the appropriate formation of these films. The treatment given to the film before the surface coating with aluminum particularly affects the properties of adhesion between substrate and deposit, is going to influence the rate of diffusion of oxygen and vapor water. In this work the bi-axial oriented polypropylene films, with a single formulation and plasma pre-treatment before the metallization, coated with aluminum were characterized, looking for, among all the possible causes the most influence on the rate of diffusion to the oxygen and water vapor. This was done, first characterizing with differential scanning calorimetry (DSC), the raw materials used in production of the samples utilized and second trials with scanning electronic microscopy (SEM), X-Ray Diffraction, Atomic force microscopy (AFM), barrier test according to ASTM D3985 and ASTM F1249.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Almanza Montero, Ovidio
Información adicional:Magister en Ingeniería: Materiales y Procesos
Palabras clave:BOPP; Polipropileno; Recubrimiento; Aluminio; Película / Polypropylene; Coating; Aluminum; Thin film
Temática:5 Ciencias naturales y matemáticas / Science > 53 Física / Physics
6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Bogotá > Facultad de Ingeniería > Departamento de Ingeniería Mecánica y Mecatrónica > Ingeniería Mecánica
Sede Medellín > Facultad de Minas > Escuela de Mecatrónica > Ingeniería Mecánica
Código ID:4099
Enviado por : Universidad Nacional de Colombia Biblioteca Digital - Sede Bogotá
Enviado el día :17 Agosto 2011 14:45
Ultima modificación:17 Agosto 2011 14:45
Ultima modificación:17 Agosto 2011 14:45
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox