Producción y caracterización de películas delgadas de YBaCo4O7+δ por medio de pulverización catódica (sputtering) a presiones altas de oxígeno

Montoya Carvajal, Juan Fernando (2010) Producción y caracterización de películas delgadas de YBaCo4O7+δ por medio de pulverización catódica (sputtering) a presiones altas de oxígeno. Maestría thesis, Universidad Nacional de Colombia. Sede Medellín.

Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.



The successful growth of thin films of the novel cobaltite YBaCo4O7+ δ by dc sputtering technique at high oxygen pressure onto r (1012) sapphire substrates is reported. The films were characterized after their structural, morphological, electrical, magnetic and optic properties. X-ray diffraction analysis showed a rather textured growth on the r-sapphire substrates. Despite the high growth temperature (850 ºC) no indication of interface reaction (formation of BaAlO4 or Y2O3) was detected. Measurements of the resistivity as a function of the temperature revealed a semiconductor like character of the as grown films. No indication of possible transitions was observed in the temperature range 300-50 K. The electronic transport mechanism seemed to be dominated by Mott variable range hopping (VRH) conduction. Fitting the VRH model to the experimental data allowed for estimating the density of states of the material at the Fermi level N(EF). The resistivity measured in magnetic fields as strong as 5 T increased notably and positive magnetoresistance values as high as ~60 % at 100 K were obtained. Magnetization measurements showed well defined hysteresis loops at 300 K and 5 K. Nevertheless, the calculate values of the magnetization resulted to be too small for the ferro- or ferrimagnetic states. Raman spectra, in turn, allowed for identifying bands associated with vibrating modes of CoO4 and YO6 in tetrahedral and octahedral configuration, respectively. Additional bands which seemed to stem from Co ions in octahedral configuration were also clearly identified. Finally, measurements of transmittance and reflectance showed intense activity of the films in the infrared region with two well defined energy gaps at 3.7 and 2.2 eV.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Morán Campaña, Oswaldo
Palabras clave:Cobaltito; Propiedades eléctricas; Propiedades magnéticas; Pulverización Catódica
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas
Código ID:3710
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :29 Jun 2011 14:05
Ultima modificación:29 Jun 2011 14:05
Ultima modificación:29 Jun 2011 14:05
Exportar:Clic aquí
Estadísticas:Clic aquí

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox