Relación entre microestructura y resistencia a corrosión de la aleación biocompatible ti6al4v deformada en caliente

Córdoba Román, Laura Catalina (2009) Relación entre microestructura y resistencia a corrosión de la aleación biocompatible ti6al4v deformada en caliente. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

2MB

Resumen

Se estudió el efecto de la microestructura sobre la resistencia a corrosión de la aleación biocompatible Ti6Al4V ELI sometida a un proceso de deformación plástica a diferentes niveles de temperatura. Se deformaron muestras a 900, 950 y 1000°C con una velocidad de avance de la herramienta de 1.8 mm/s. Se emplearon las técnicas de microscopía óptica y microscopía electrónica de barrido para la caracterización microestructural, así como las técnicas de análisis digital de imágenes y difracción de rayos X para la cuantificación de las fases. Se realizaron curvas de polarización cíclica en solución Ringer desaireada para la evaluación de la resistencia a corrosión con el fin de determinar si existía o no una dependencia de esta propiedad con la temperatura de deformación. Las superficies ensayadas fueron analizadas en microscopio electrónico para evaluar el deterioro de la superficie. El material presentó mejores propiedades de formabilidad a 1000°C, temperatura perteneciente al campo monofásico (β) de la aleación. Para las temperaturas correspondientes al intervalo bifásico (α+β) el material mostró una mayor resistencia a la deformación corroborando la dependencia del esfuerzo de flujo con la temperatura. A partir de las curvas de polarización cíclica fue posible medir el potencial de corrosión (Ec) y la resistencia a la polarización (Rp) siendo este último el factor determinante de la resistencia a corrosión de la aleación Ti6Al4V ELI. Los valores encontrados para estas dos variables fueron correlacionados con las características microestructurales del material. / Abstract. The effect of the microstructure on the corrosion resistance of the hot formed Ti6Al4V ELI alloy was studied. Samples were forged at 900, 950 and 1000°C with a constant tool speed of 1.8 mm/s. Optical and Scanning Electron Microscopy techniques were employed to determine the microstructure features. A quantitative analysis was made using digital image processing and X-ray diffraction techniques. The corrosion resistance of the alloy was evaluated by mean of cyclic polarization tests on Ringer’s solution to determine the possible effect of the forging temperature. Tested surfaces were analyzed by Scanning Electron Microscopy to evaluate the surface damage. Material showed the better flow behavior at the highest tested temperature corresponding to the single phase field (β) at 1000°C. Temperatures tested in the dual phase field (α+β) showed higher deformation resistance indicating the dependence of the flow stress on working temperature. Potential corrosion (Ec) and polarization resistance (Rp) were measured from polarization curves being the latter one the major indicator who determined the corrosion resistance of Ti6Al4V ELI alloy.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Toro Betancur, Alejandro
Palabras clave:Microestructura; Resistencia a la corrosión
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Ingeniería de Materiales
Código ID:2303
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :24 Noviembre 2010 18:36
Ultima modificación:15 Febrero 2011 01:28
Ultima modificación:15 Febrero 2011 01:28
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox