Identificación y cuantificación de fases en acero inoxidable ASTM A743 grado CA6NM mediante la técnica de difracción de rayos x

Rojas Marín, Jessika Viviana (2009) Identificación y cuantificación de fases en acero inoxidable ASTM A743 grado CA6NM mediante la técnica de difracción de rayos x. Maestría thesis, Universidad Nacional de Colombia.

Texto completo

[img]
Vista previa
PDF - Versión Aceptada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

1MB

Resumen

La técnica de difracción de rayos X a altas temperaturas fue aplicada al estudio de las transformaciones de fase en el acero inoxidable martensítico ASTM A743 grado CA6NM, material ampliamente usado en la fabricación de componentes hidráulicos por las excelentes propiedades mecánicas que ofrece. Mediante la técnica de difracción de rayos X y en el intervalo de temperaturas entre 25-860°C se estudió la dilatación térmica del acero durante el calentamiento, se identificaron las temperaturas de transformación de fase así como la evolución isotérmica de las fases presentes a diferentes temperaturas. Se presenta una metodología para la identificación y cuantificación de fases en el acero ASTM A743 grado CA6NM por el método de comparación directa a partir de los difractogramas obtenidos a temperaturas de 580, 600, 620, 640, 660, 680, 700°C y a temperatura ambiente posterior a tratamientos térmicos de revenido a éstas temperaturas. Se observó un aumento en la fracción volumétrica de austenita retenida con tratamientos térmicos de revenido realizados entre 580 y 620°C donde se observó en la microestructura una martensita más fina y homogénea. Los resultados obtenidos fueron validados con análisis dilatométricos previos. / Abstract.High temperature X-ray diffraction was used for studying phase transformations in an ASTM A743 grade CA6NM cast martensitic stainlees steel, which is widely used for manufacturing hydraulic components due to their excellent mechanical properties related to the amount of retained austenite in the microstructure. Through X ray diffraction in the range between 25-860°C was analyzed thermal expansion during heating and phase transformation temperatures were identified, as well as the isothermal phase evolution at several temperatures. A methodology to precisely identify and quantify phases in ASTM A743 grade CA6NM martensitic stainless steel at 580, 600, 620, 640, 660, 680 and 700°C using the direct comparison method was developed and used to determine the amount of the retained austenite in the microstructure at room temperature after diferent tempering treatments. The volume fraction of retained austenite increased with tempering treatments performed in the range between 580-620°C, in which a refined and more homogeneous martensite was obtained. The results obtained by X-ray diffraction were compared to and validated with dilatometric measurements.

Tipo de documento:Tesis/trabajos de grado - Thesis (Maestría)
Colaborador / Asesor:Toro Betancur, Alejandro
Palabras clave:Difracción de rayos X; Acero - Tratamiento térmico; Transformaciones martensiticas
Temática:6 Tecnología (ciencias aplicadas) / Technology > 62 Ingeniería y operaciones afines / Engineering
Unidad administrativa:Sede Medellín > Facultad de Minas > Escuela de Procesos y Energía
Código ID:2161
Enviado por : Biblioteca Sede Medellín Universidad Nacional de Colombia
Enviado el día :22 Oct 2010 01:49
Ultima modificación:11 Oct 2012 20:47
Ultima modificación:11 Oct 2012 20:47
Exportar:Clic aquí
Estadísticas:Clic aquí
Compartir:

Solamente administradores del repositorio: página de control del ítem

Vicerrectoría de Investigación: Número uno en investigación
Indexado por:
Indexado por Scholar Google WorldCat DRIVER Registry of Open Access Repositories OpenDOAR Metabiblioteca BDCOL OAIster Red de repositorios latinoamericanos DSpace BASE Open archives La referencia Colombiae Open Access Theses and Dissertations Tesis latinoamericanas CLACSO
Este sitio web se ve mejor en Firefox